| K Monel 500 |
| *trademark Huntington Alloys |
|
|
|
|
|
|
|
|
|
|
|
|
| K-500 Alloy has similar properties to Monel 400 Alloy, but has the added feature of Age Hardening to achieve a higher strength and hardness, This is due to the addition of aluminium and titanium. K-500 Alloys strength is maintained to temperatures as high as 1200 F, yet stays tough and ductile to temperatures down to -423 F. Along with staying non-magnetic down to -210 F. A common specification for this is QQ N 286. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Comp. % |
| 63.0 min. |
| 2.0 max. |
| 1.5 max. |
| 2.3-3.15 |
|
|
|
|
|
|
|
|
|
|
|
| Comp. % |
| .18 max. |
| 27.0-33.0 |
| .50 max. |
| .01 max. |
| .35-.85 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Density/lbs/cu in. |
| Modulus of elasticity,psi |
| Tension |
| Torsion |
| Poisson Ratio |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| .298 |
|
| 31,000,000 |
| 11,000,000 |
| .29 |
|
|
|
|
|
|
|
|
|
|
|
| Tensiles per QQ N 281 Class A |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| Cold drawn, as drawn, all sizes |
| Cold drawn, and annealed, all sizes |
| Cold drawn, spring temper as drawn |
| .057 and less |
| Over .057 to .114 |
| Over .114 to .229 |
| Over .229 to .312 |
|
|
|
|
|
|
|
|
|
| 110,000-155,000 |
| 110,000 min. |
|
| 165,000 min. |
| 155,000 min. |
| 150,000 min. |
| 145,000 min. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| 1000 F hold for 8-16 hours (depends on desired hardness after aging). Furnace cool to aim temperature 900 F then air cool. |
|
|
|
|
|
|
|
|
|
|
|
|
|
| Cold drawn,as drawn age hardened: |
| All sizes |
| Cold drawn ,spring temper, and age hardened: |
| .114 and less |
| over .114 to .375 |
|
|
|
|
|
|
|
|
|
|
|
|
| 155,000 min. |
|
| 180,000 min. |
| 170,000 min. |
|
|
|
|
|
|
|
|
|
|
| The information and data presented herein are typical or average values and are not guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
 |
|
 |
|
|
 |
|
|
 |
|
|
|
|
|
|
|
|
|
|
|
|
|
|